2024 T3 Aerospace Grade Aluminum Alloy Sheet Plate 1.5mm-150mm Thickness for Aircraft Structural Components
| Herkunftsort | Shandong, China |
|---|---|
| Markenname | Hongtu |
| Zertifizierung | ISO 9001:2015, SGS, AMS-QQ-A-250/4 |
| Modellnummer | 2024-T3 |
| Min Bestellmenge | 500 KG |
| Preis | USD 3.5-5.8 / kg |
| Verpackung Informationen | Mit Rostschutzpapier verschachtelte Holzpalette in Exportqualität mit Stahlumreifung und feuchtigkei |
| Lieferzeit | 5–7 Werktage für den Lagerbestand, 15–25 Tage für die Produktion |
| Zahlungsbedingungen | T/T, L/C, Paypal, Western Union |
| Versorgungsmaterial-Fähigkeit | 2000 Tonnen pro Monat |
Produktdetails
| Legierung | 2024 | Temperament | T3, T351, T4 |
|---|---|---|---|
| Dicke | 1,5 mm - 150 mm | Breite | 1000 mm, 1250 mm, 1500 mm, 2000 mm, 2500 mm |
| Länge | 2000 mm, 2440 mm, 3000 mm, 6000 mm oder kundenspezifisch | Standard | ASTM B209, AMS 4035, AMS 4037, EN 573 |
| Oberflächenbeschaffenheit | Mühlenfinish, eloxiert, beschichtet, poliert | Zugfestigkeit | ≥ 485 MPa |
| Streckgrenze | ≥ 345 MPa | Verlängerung | ≥ 12% |
| Anwendung | Flugzeugstrukturen, Rumpf, Flügelholme, Ausrüstung | ||
| Hervorheben | 2024 T3 Aerospace Aluminum Sheet,Aircraft Grade Alloy Plate 2024,High Strength Aviation Aluminum Plate |
||
Produkt-Beschreibung
2024 T3 Aerospace Grade Aluminum Alloy Sheet Plate 1.5mm-150mm Thickness for Aircraft Structural Components
2024 T3 Aerospace Grade Aluminum Alloy Sheet Plate
The 2024 T3 aluminum alloy sheet is a high-strength, heat-treatable alloy renowned for its excellent strength-to-weight ratio and superior fatigue resistance. Widely used in aerospace and aviation industries, this alloy delivers reliable performance in demanding structural applications.
Key Features
- High Strength: Tensile strength ≥ 485 MPa in T3 temper, rivaling mild steel strength with 1/3 the weight
- Excellent Fatigue Resistance: Engineered to withstand repeated stress cycles in aircraft applications
- Good Machinability: Superior cutting and forming characteristics for complex component manufacturing
- Heat Treatable: Solution heat-treated and cold-worked for enhanced mechanical properties
- Natural Aging: Stable mechanical properties achieved through natural aging process
Chemical Composition (Weight %)
| Element | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Al |
|---|---|---|---|---|---|---|---|---|---|
| Min | - | - | 3.8 | 0.3 | 1.2 | - | - | - | Remainder |
| Max | 0.50 | 0.50 | 4.9 | 0.9 | 1.8 | 0.10 | 0.25 | 0.15 |
Mechanical Properties (T3 Temper)
| Property | Value |
|---|---|
| Tensile Strength | ≥ 485 MPa |
| Yield Strength | ≥ 345 MPa |
| Elongation | ≥ 12% |
| Hardness (Brinell) | 120 HB |
| Density | 2.78 g/cm³ |
Available Dimensions
| Parameter | Range |
|---|---|
| Thickness | 1.5mm - 150mm |
| Width | 1000mm - 2500mm |
| Length | 2000mm - 6000mm or Custom |
| Temper | T3, T351, T4, T42 |
Applications
- Aircraft fuselage skins and structural panels
- Wing spars, ribs and stringers
- Vehicle armor plates
- High-performance truck wheels
- Precision machined components and fittings
Our Advantages
- Strict Quality Control: Every batch undergoes spectrographic analysis, tensile testing and ultrasonic inspection
- Complete Traceability: Mill test certificates (MTC EN 10204 3.1) provided with every shipment
- Flexible MOQ: Small trial orders accepted from 500 kg
- Professional Packaging: Export-grade wooden pallets with anti-corrosion paper and PE film wrapping
- Fast Delivery: Extensive stock inventory for prompt shipment; custom production within 15-25 days
Contact us today for a competitive quotation, free sample cutting, and technical consultation on 2024 T3 aerospace aluminum sheets.